Critical Surface Tension Components (ascending sfe sort)

This table is provided as an information service by Diversified Enterprises.

This table highlights the critical surface tension, surface free energy, contact angles with water, and Hansen Solubility Parameters with interaction radius for a variety of polymers. For all columns except polymer name, CAS #, change in surface tension per degree Celsius (dγ/dt), and total Hansen Solubility Parameter (δ) the first row of data for each material is the average of surveyed values; the second row shows the standard deviation, with the number of data points (n) in parentheses. For n = 1, no standard deviation figure is shown. Click on any column's footnote for details. Click on any polymer name for original research results. An analogous table, which shows polar/dispersion and acid—base components of surface energy, can be seen here. Comments on methodology and the like can be found here.

This table can be sorted by column — just click on the column header as desired to re-order this printable table. Click on any footnote for additional information.

Some print software will automatically scale this page so that it prints well with “portrait” orientation. If your printer doesn't have this feature, you will want to change your print set-up to “landscape” orientation prior to printing.

print this sort order (table and references - will open new browser window)

Critical Surface Tension, Surface Free Energy, Contact Angles with Water, and Hansen Solubility Parameters for Various Polymers

Name⁽¹⁾	CAS #⁽²⁾	γ_c⁽³⁾	γ_S⁽⁴⁾	dγ/dt⁽⁵⁾	θ_W^Y⁽⁶⁾	θ_W^A⁽⁷⁾	θ_W^R⁽⁸⁾	dθ_W ⁽⁹⁾	δ⁽¹⁰⁾	δ_D⁽¹¹⁾	δ_P⁽¹²⁾	δ_H⁽¹³⁾	R_o⁽¹⁴⁾
Amorphous fluoropolymer (Teflon AF)	-	-	-	-	-	117.5	90.3	27.1	-	-	-	-	-
Amorphous fluoropolymer (Teflon AF)						5.67(5)	3.42(5)	9.13(5)
Cellulose triacetate	9012-09-3	48.8	-	-	-	-	-	-	-	-	-	-	-
Cellulose triacetate		-(1)
Nafion	31175-20-9	-	-	-	-	90.5	-	-	-	-	-	-	-
Nafion						4.80(4)
Nylon 7,7	-	43.0	-	-	-	70.0	-	-	-	-	-	-	-
Nylon 7,7		-(1)				-(1)
Nylon 8,8	-	34.0	-	-	-	86.0	-	-	-	-	-	-	-
Nylon 8,8		-(1)				-(1)
Nylon 9,9	-	34.0	-	-	-	86.0	-	-	-	-	-	-	-
Nylon 9,9			-(1)				-(1)
Nylon 10,10	-	32.0	-	-	-	94.0	-	-	-	-	-	-	-
Nylon 10,10		-(1)				-(1)
Polybenzyl methacrylate (PBMA)	25085-83-0	36.0	-	-	-	-	-	-	-	-	-	-	-
Polybenzyl methacrylate (PBMA)		-(1)
Polyetherimide (PEI)	61128-46-9	-	-	-	76.5	-	-	-	19.8	17.7	6.0	6.4	4.8
Polyetherimide (PEI)					12.0(2)					1.07(5)	1.14(5)	2.43(5)	1.70(5)
Poly(2-hydroxyethyl methacrylate)	24249-16-5	37.0	-	-	-	-	-	-	-	-	-	-	-
Poly(2-hydroxyethyl methacrylate)		-(1)
Polyoctyl methacrylate	-	23.5	-	-	-	-	-	-	-	-	-	-	-
Polyoctyl methacrylate		-(1)
Polyphenyl methacrylate	-	35.0	-	-	-	-	-	-	-	-	-	-	-
Polyphenyl methacrylate		-(1)
Polyvinyl formal	63450-15-7	39.0	-	-	-	-	-	-	-	-	-	-	-
Polyvinyl formal		-(1)
Poly(heptafluoroisopropyl acrylate)	-	-	14.0	-	-	-	-	-	-	-	-	-	-
Poly(heptafluoroisopropyl acrylate)			-(1)
Poly(nonafluoroisobutyl acrylate)	-	-	14.0	-	-	-	-	-	-	-	-	-	-
Poly(nonafluoroisobutyl acrylate)			-(1)
Poly(heptafluoroisopropyl methacrylate)	-	-	15.0	-	-	-	-	-	-	-	-	-	-
Poly(heptafluoroisopropyl methacrylate)			-(1)
Poly(heptadecafluorooctyl methacrylate)	-	-	15.3	-	-	-	-	-	-	-	-	-	-
Poly(heptadecafluorooctyl methacrylate)			-(1)
Poly(phosphazene)	-	16.5	15.8	-	-	-	-	-	-	-	-	-	-
Poly(phosphazene)		-(1)	0.35(2)
Poly(hexafluoropropylene)	-	16.9	15.9	-	112.0	-	-	-	-	-	-	-	-
Poly(hexafluoropropylene)		0.96(3)	2.67(4)		-(1)
Fluorinated ethylene polypropylene (FEP)	25067-11-2	19.1	18.5	-	105.7	112.7	98.5	14.8	19.6	19.0	4.0	3.0	4.0
Fluorinated ethylene polypropylene (FEP)		1.27(2)	2.25(7)		4.54(6)	5.03(4)	5.28(4)	1.31(3)		-(1)	-(1)	-(1)	-(1)
Polydimethylsiloxane (PDMS)	9016-00-6	20.1	20.4	-0.048^(b)	107.8	107.0	69.1	39.3	-	-	-	-	-
Polydimethylsiloxane (PDMS)		3.17(7)	1.54(26)		8.78(3)	4.44(9)	7.10(7)	3.73(7)
Polytetrafluoroethylene (PTFE)	9002-84-0	19.4	21.8	-0.058^(c)	109.4	108.9	96.0	14.3	16.7	16.2	1.8	3.4	3.9
Polytetrafluoroethylene (PTFE)		1.49(8)	3.24(35)		5.70(17)	7.06(8)	8.72(3)	10.6(3)		-(1)	-(1)	-(1)	-(1)
Hexatriacontane	630-06-8	20.6	22.8	-0.066^(c)	108.2	109.0	-	-	-	-	-	-	-
Hexatriacontane		1.30(6)	5.03(9)		4.03(2)	-(1)
Poly(4-methyl pentene-1)	-	-	25.0	-	-	-	-	-	-	-	-	-	-
Poly(4-methyl pentene-1)			-(1)
Polydiethylsiloxane (PDES)	63148-61-8	-	25.7	-0.073^(c)	-	-	-	-	-	-	-	-	-
Polydiethylsiloxane (PDES)			-(1)
Polymethylphenylsiloxane	9005-12-3	-	26.1	-	-	-	-	-	-	-	-	-	-
Polymethylphenylsiloxane			-(1)
Polytrifluoroethylene	24980-67-4	26.5	26.5	-	92.0	-	-	-	-	-	-	-	-
Polytrifluoroethylene		3.99(3)	2.79(7)		-(1)
Paraffin	8002-74-2	24.8	27.9	-0.060^(c)	109.3	108.5	96.0	11.0	-	-	-	-	-
Paraffin		6.53(3)	3.96(12)		1.84(2)	2.12(2)	-(1)	-(1)
Polyvinyl octanoate	-	-	28.7	-0.061^(c)	-	-	-	-	-	-	-	-	-
Polyvinyl octanoate			-(1)
Poly 2-ethylhexyl methacrylate	25719-51-1	-	28.8	-0.062^(c)	-	-	-	-	-	-	-	-	-
Poly 2-ethylhexyl methacrylate			-(1)
Eicosane	112-95-8	-	28.9	-0.0833^(c)	-	-	-	-	-	-	-	-	-
Eicosane			-(1)
Polyvinyl decanoate	-	-	28.9	-0.062^(c)	-	-	-	-	-	-	-	-	-
Polyvinyl decanoate			-(1)
Polyvinyl hexanoate	-	-	28.9	-0.063^(c)	-	-	-	-	-	-	-	-	-
Polyvinyl hexanoate			-(1)
Polyvinyl dodecanoate	-	-	29.1	-0.063^(c)	-	-	-	-	-	-	-	-	-
Polyvinyl dodecanoate
Poly 2-ethylhexyl acrylate	9003-77-4	31.0	29.7	-0.070^(c)	-	-	-	-	-	-	-	-	-
Poly 2-ethylhexyl acrylate		-(1)	0.71(2)
Poly(hexyl methacrylate)	25087-17-6	27.5	30.0	-0.062^(c)	-	-	-	-	-	-	-	-	-
Poly(hexyl methacrylate)		-(1)	0.00(2)
Polypropylene (PP)	^(a)	30.5	30.2	-0.058^(b)	94.9	107.3	89.0	20.2	18.0	17.7	2.9	1.2	6.2
Polypropylene (PP)		1.50(3)	2.77(32)		5.29(11)	7.75(15)	5.73(6)	2.72(6)		0.46(2)	2.80(2)	1.71(2)	1.76(2)
Ethyl cellulose	9004-57-3	-	30.3	-	-	84.5	-	-	20.4	19.0	5.6	4.9	7.9
Ethyl cellulose			2.40(2)			-(1)				1.56(2)	1.84(2)	1.41(2)	2.83(2)
Poly t-butyl methacrylate (PtBMA)	25189-00-9	18.1	30.5	-0.059^(b)	108.1	-	-	-	-	-	-	-	-
Poly t-butyl methacrylate (PtBMA)		-(1)	0.00(2)		-(1)
Polypropylene glycol (PPG, polypropylene oxide)	25322-69-4	32.0	30.6	-0.079^(b)	-	-	-	-	-	-	-	-	-
Polypropylene glycol (PPG, polypropylene oxide)		-(1)	2.36(7)
Polychlorotrifluoroethylene (PCTFE)	9002-83-9	30.8	30.7	-0.067^(c)	90.0	104.0	72.0	32.0	16.5	15.6	2.5	4.7	5.8
Polychlorotrifluoroethylene (PCTFE)		1.34(4)	3.79(7)		-(1)	0.00(2)	7.07(2)	7.07(2)		2.10(3)	1.46(3)	2.44(3)	1.56(3)
Poly iso-butyl methacrylate (PIBMA)	9011-15-8	-	30.9	-0.060^(b)	-	-	-	-	20.0	18.3	4.9	6.3	9.4
Poly iso-butyl methacrylate (PIBMA)			0.00(2)							2.11(3)	0.93(3)	5.12(3)	2.10(3)
Polyvinyl hexadecanoate	-	-	30.9	-0.066^(c)	-	-	-	-	-	-	-	-	-
Polyvinyl hexadecanoate			-(1)
Thermoplastic polyolefin (TPO)	-	-	30.9	-	-	101.5	79.0	22.5	-	-	-	-	-
Thermoplastic polyolefin (TPO)			3.45(11)			3.54(2)	7.07(2)	3.54(2)
Polyvinyl butyrate	-	-	31.1	-0.070^(c)	-	-	-	-	-	-	-	-	-
Polyvinyl butyrate			-(1)
Polyvinylidene fluoride (PVDF)	24937-79-9	31.6	31.5	-	86.0	93.4	91.0	1.0	23.2	17.0	12.1	10.2	4.1
Polyvinylidene fluoride (PVDF)		5.83(5)	5.29(13)		4.00(3)	1.98(2)	-(1)	-(1)		-(1)	-(1)	-(1)	-(1)
Polytetrahydrofuran (PTHF)	25190-06-1	-	31.9	-	-	-	-	-	-	-	-	-	-
Polytetrahydrofuran (PTHF)			0.00(2)
Polyisoprene (PIP)	9003-31-0	-	32.3	-	-	-	-	-	18.4	18.1	2.4	2.3	10.3
Polyisoprene (PIP)			1.53(3)							2.32(3)	1.40(3)	2.66(3)	3.40(3)
Ethylene-propylene-diene-monomer (EPDM)	25038-36-2	-	32.5	-	91.0	-	-	-	-	-	-	-	-
Ethylene-propylene-diene-monomer (EPDM)		4.31(2)		-(1)
Poly n-butyl acrylate	9003-49-0	29.5	32.8	-0.070^(c)	-	-	-	-	-	-	-	-	-
Poly n-butyl acrylate		2.12(2)	1.82(3)
Polylauryl methacrylate	25719-52-2	21.3	32.8	-	-	-	-	-	-	-	-	-	-
Polylauryl methacrylate		-(1)	-(1)
Polytetramethylene oxide	-	-	32.8	-	-	-	-	-	-	-	-	-	-
Polytetramethylene oxide			1.27(2)
Poly n-butyl methacrylate (PnBMA)	25608-33-7	29.8	33.1	-0.059^(b)	91.0	-	-	-	18.4	16.0	6.2	6.6	9.5
Poly n-butyl methacrylate (PnBMA)		1.94(3)	2.70(12)		-(1)					-(1)	-(1)	-(1)	-(1)
Polyisobutylene (PIB, butyl rubber)	9003-27-4	27.0	33.2	-0.064^(b)	-	112.1	-	-	17.1	16.4	1.7	4.7	7.9
Polyisobutylene (PIB, butyl rubber)		0.00(2)	3.21(10)			-(1)				1.26(6)	2.15(6)	2.08(6)	2.46(6)
Poly n-propyl methacrylate	2210-79-9	32.0	33.2	-0.065^(c)	-	-	-	-	-	-	-	-	-
Poly n-propyl methacrylate		-(1)	-(1)
Polyethylene (PE)	9002-88-4	31.6	33.5	-0.057^(b)	94.9	97.2	83.1	13.9	17.6	16.8	3.8	3.8	6.6
Polyethylene (PE)		2.05(21)	3.02(62)		6.96(27)	5.80(26)	10.7(9)	8.66(9)		0.88(7)	1.94(7)	2.52(7)	2.84(7)
Cellulose acetate butyrate (CAB)	9004-36-8	-	34.0	-	-	-	-	-	22.2	17.2	13.8	2.8	12.6
Cellulose acetate butyrate (CAB)			-(1)							-(1)	-(1)	-(1)	-(1)
Nylon 11	25587-80-8	35.6	34.0	-	-	82.0	-	-	20.5	17.0	4.4	10.6	5.1
Nylon 11		4.40(8)	-(1)			9.90(2)				-(1)	-(1)	-(1)	-(1)
Polyethyl methacrylate (PEMA)	9003-42-3	32.8	34.0	-0.070^(c)	-	-	-	-	20.0	17.5	8.5	4.7	9.6
Polyethyl methacrylate (PEMA)		0.90(4)	2.50(7)							1.34(3)	0.62(3)	3.82(3)	1.99(3)
Polyvinyl proprionate	25035-84-1	-	34.0	-0.072^(c)	-	-	-	-	-	-	-	-	-
Polyvinyl proprionate			-(1)
Polyethyl acrylate (PEA)	9003-32-1	34.0	35.1	-0.070^(c)	-	-	-	-	-	-	-	-	-
Polyethyl acrylate (PEA)		1.41(2)	1.47(6)
Poly(dimethylaminoethyl methacrylate)	-	-	36.0	-	-	-	-	-	-	-	-	-	-
Poly(dimethylaminoethyl methacrylate)			-(1)
Polyvinyl ethyl ether (polyethoxyethylene)	25104-37-4	-	36.0	-	-	-	-	-	-	-	-	-	-
Polyvinyl ethyl ether (polyethoxyethylene)			-(1)
Polystearyl methacrylate	25639-21-8	20.8	36.3	-	-	-	-	-	-	-	-	-	-
Polystearyl methacrylate		-(1)	-(1)
Polyvinyl fluoride (PVF)	24981-14-4	32.7	36.4	-	82.5	88.6	-	-	-	-	-	-	-
Polyvinyl fluoride (PVF)		4.66(4)	4.07(14)		3.54(2)	-(1)
Polyurethanes	-	-	37.5	-	77.5	83.1	35.5	47.4	22.8	18.8	10.0	8.2	9.8
Polyurethanes			4.01(11)		7.52(8)	14.2(9)	16.3(9)	21.7(9)		1.53(11)	2.54(11)	3.09(11)	3.48(11)
Polyvinyl butyral	63148-65-2	28.0	38.0	-	-	-	-	-	24.6	19.1	9.5	12.2	10.0
Polyvinyl butyral		-(1)	-(1)							0.92(3)	4.50(3)	1.65(3)	1.53(3)
Polystyrene (PS)	9003-53-6	34.0	38.3	-0.072^(b)	85.3	88.5	81.8	10.0	23.9	22.8	5.8	4.3	12.7
Polystyrene (PS)		4.27(18)	5.23(32)		6.08(8)	5.75(15)	3.86(4)	2.65(3)		-(1)	-(1)	-(1)	-(1)
Polyvinyl acetate (PVA)	9003-20-7	35.3	38.5	-0.066^(b)	60.6	-	-	-	25.7	20.9	11.3	9.7	13.7
Polyvinyl acetate (PVA)		2.08(3)	2.75(14)		-(1)					-(1)	-(1)	-(1)	-(1)
Polyoxymethylene (POM, polyacetal, polymethylene oxide)	24969-26-4	37.0	38.6	-	74.5	79.0	54.0	25.0	-	-	-	-	-
Polyoxymethylene (POM, polyacetal, polymethylene oxide)		1.41(2)	5.68(3)		-(1)	-(1)	-(1)	-(1)
Poly a-methyl styrene	25014-31-7	-	38.7	-0.058^(b)	-	-	-	-	-	-	-	-	-
Poly a-methyl styrene			-(1)
Nylon 12	24937-16-4	37.1	39.3	-	-	72.4	56.5	20.5	22.2	18.5	8.1	9.1	6.3
Nylon 12		8.63(2)	3.02(3)			5.37(3)	-(1)	-(1)		-(1)	-(1)	-(1)	-(1)
Polymethyl acrylate (PMA)	25087-26-7	38.0	39.8	-0.070^(c)	-	-	-	-	-	-	-	-	-
Polymethyl acrylate (PMA)		4.24(2)	2.21(9)
Polyvinyl chloride (PVC)	9002-86-2	37.9	40.1	-	83.2	91.9	75.3	-	20.0	16.8	8.9	6.1	8.5
Polyvinyl chloride (PVC)		7.05(11)	3.66(22)		10.3(8)	7.88(3)	-(1)			1.65(5)	1.95(5)	1.78(5)	3.94(5)
Nylon 6,10	9008-66-6	-	40.5	-	-	71.0	-	-	-	-	-	-	-
Nylon 6,10			-(1)			-(1)
Polychloroprene	9010-98-4	38.0	40.9	-0.086^(b)	-	-	-	-	-	-	-	-	-
Polychloroprene		0.00(2)	3.63(7)
Cellulose acetate (CA)	9004-35-7	37.5	41.1	-	54.5	-	-	-	23.5	17.1	13.1	9.4	10.6
Cellulose acetate (CA)		2.12(2)	3.37(5)		-(1)					1.58(4)	4.41(4)	3.81(4)	2.96(4)
Aluminum foil ^(f)	7429-90-5	-	41.2	-	81.3	-	-	-	-	-	-	-	-
Aluminum foil ^(f)			2.47(2)		4.60(2)	-	-	-	-	-	-	-	-
Poly(hexachlorobutadiene)	-	-	41.5	-	-	-	-	-	-	-	-	-	-
Poly(hexachlorobutadiene)			-(1)
Polymethyl methacrylate (PMMA, acrylic, plexiglas)	9011-14-7	37.5	41.8	-0.076^(b)	69.1	74.7	54.2	18.4	21.3	17.9	10.1	5.4	11.0
Polymethyl methacrylate (PMMA, acrylic, plexiglas)		4.68(12)	3.63(38)		6.08(17)	10.2(8)	5.44(2)	1.98(2)		1.37(5)	4.46(5)	3.73(5)	4.63(5)
Acrylonitrile butadiene styrene (ABS)	9003-56-9	38.5	42.0	-	89.7	72.0	-	-	19.2	17.0	5.7	6.8	9.4
Acrylonitrile butadiene styrene (ABS)		-(1)	4.70(8)		-(1)	-(1)				0.92(2)	4.17(2)	0.49(2)	2.19(2)
Ethyl methacrylate (EMA)	97-63-2	-	42.0	-	-	74.0	-	-	-	-	-	-	-
Ethyl methacrylate (EMA)			1.06(2)			-(1)
Polyetheretherketone (PEEK)	29658-26-2	-	42.1	-	91.0	85.0	55.0	30.0	-	-	-	-	-
Polyetheretherketone (PEEK)			-(1)		-(1)	-(1)	-(1)	-(1)
Polycarbonate (PC)	24936-68-3	44.0	42.3	-0.060^(c)	81.3	84.0	68.0	16.0	22.2	19.6	8.8	5.7	10.2
Polycarbonate (PC)		2.83(2)	5.32(7)		5.77(3)	-(1)	-(1)	-(1)		1.75(3)	2.58(3)	1.04(3)	4.06(3)
Polymethacrylonitrile (PMAN)	25067-61-2	39.0	42.3	-	-	-	-	-	23.7	17.2	14.4	7.6	3.8
Polymethacrylonitrile (PMAN)		-(1)	3.08(3)							-(1)	-(1)	-(1)	-(1)
Nitrocellulose (cellulose nitrate)	9004-70-0	-	42.7	-	-	54.7	20.0	34.7	23.5	16.2	14.1	9.5	10.7
Nitrocellulose (cellulose nitrate)			4.10(3)			11.0(3)	22.5(3)	12.1(3)		1.06(2)	0.85(2)	1.06(2)	1.13(2)
Phenoxy resin	26402-79-9	-	43.0	-	-	-	-	-	-	-	-	-	-
Phenoxy resin			-(1)
Polyethylene oxide (PEO, PEG, polyethylene glycol)	25322-68-3	43.0	43.1	-0.095^(c)	63.0	-	-	-	-	-	-	-	-
Polyethylene oxide (PEO, PEG, polyethylene glycol)		-(1)	2.07(16)		-(1)
Polyepichlorohydrin	24969-06-0	35.0	43.2	-	-	-	-	-	-	-	-	-	-
Polyepichlorohydrin		0.00(2)	-(1)
Polymethylphenylsilylene	-	-	43.7	-	-	-	-	-	-	-	-	-	-
Polymethylphenylsilylene			0.57(2)
Polyvinylidene chloride (PVDC, Saran)	9002-85-1	40.2	43.7	-	80.0	-	-	-	23.1	19.0	9.6	9.0	5.8
Polyvinylidene chloride (PVDC, Saran)		3.89(4)	2.81(9)		-(1)					1.98(2)	0.64(2)	1.70(2)	2.62(2)
Polyimide (PI)	25038-81-7	-	43.8	-	71.5	79.9	48.0	31.3	-	-	-	-	-
Polyimide (PI)			6.80(4)		2.07(6)	5.01(8)	12.2(8)	10.4(8)
Polyethylene terephthalate (PET)	25038-59-9	39.0	44.0	-0.065^(c)	72.0	73.0	54.5	20.0	20.8	18.7	6.3	6.7	6.5
Polyethylene terephthalate (PET)		5.71(11)	3.85(28)		6.33(17)	7.32(17)	5.77(8)	11.0(8)		1.25(8)	2.03(8)	2.80(8)	3.36(8)
Polyvinyl alcohol (PVOH)	25213-24-5	37.0	44.2	-	51.0	-	-	-	25.2	14.7	14.1	14.9	10.5
Polyvinyl alcohol (PVOH)		-(1)	6.56(4)		-(1)					2.51(4)	2.13(4)	2.18(4)	1.38(4)
Nylon 6,6	32131-17-2	42.2	44.3	-0.065^(c)	67.6	69.3	40.9	27.6	25.8	17.2	9.9	16.5	4.4
Nylon 6,6		4.50(12)	3.62(18)		4.94(7)	2.91(5)	-(1)	-(1)		1.11	1.10	6.80	1.24
Polysulfone (PSU)	25135-51-7	42.1	44.9	-	75.0	66.0	-	-	21.5	18.5	8.5	7.0	9.4
Polysulfone (PSU)		1.48(2)	2.47(2)		-(1)	-(1)				2.17(3)	2.61(3)	1.12(3)	1.69(3)
Poly(L-alanine)	25191-17-7	-	45.2	-	-	-	-	-	-	-	-	-	-
Poly(L-alanine)			-(1)
Epoxies	-	44.5	45.3	-	54.0	87.5	-	-	24.1	19.2	10.9	9.6	11.1
Epoxies		0.71(2)	4.21(6)		-(1)	3.54(2)				2.53(13)	2.37(13)	2.66(13)	3.98(13)
Cellophane	9005-81-6	-	45.4	-	-	-	-	-	28.5	16.1	18.5	14.5	9.3
Cellophane			-(1)							-(1)	-(1)	-(1)	-(1)
Nylon 6 (polycaprolactum, aramid 6)	25038-54-4	43.9	45.4	-	-	65.5	42.4	26.8	20.3	17.0	3.4	10.6	5.1
Nylon 6 (polycaprolactum, aramid 6)		2.42(3)	3.52(6)			4.27(7)	-(1)	-(1)		-(1)	-(1)	-(1)	-(1)
Aramid (Kevlar)	26125-61-1	-	45.7	-	-	63.7	-	-	-	-	-	-	-
Aramid (Kevlar)			1.76(3)			3.54(2)
Polybutadiene	9003-17-2	29.3	45.9	-0.144^(d)	96.0	-	-	-	18.0	17.5	2.3	3.4	6.6
Polybutadiene		3.79(3)	3.89(2)	-0.110^(e)	1.41(2)					-(1)	-(1)	-(1)	-(1)
Polyphenylene oxide (PPO)	25134-01-4	47.0	46.0	-	-	-	-	-	19.3	16.9	8.9	2.7	11.7
Polyphenylene oxide (PPO)		-(1)	-(1)							-(1)	-(1)	-(1)	-(1)
Polyvinyl pyrrolidone (PVP)	9003-39-8	-	46.0	-	-	-	-	-	-	-	-	-	-
Polyvinyl pyrrolidone (PVP)			3.61(2)
Polybutylene terephthalate (PBT)	26062-94-2	-	46.3	-	-	84.0	-	-	-	-	-	-	-
Polybutylene terephthalate (PBT)			0.51(5)			0.00(2)
Polyxylylene (parylene)	-	-	46.3	-	-	-	-	-	-	-	-	-	-
Polyxylylene (parylene)			-(1)
Polyacrylonitrile (PAN)	25014-41-9	47.0	46.8	-	-	-	-	-	27.4	21.7	14.1	9.1	10.9
Polyacrylonitrile (PAN)		4.24(2)	6.62(4)							-(1)	-(1)	-(1)	-(1)
Polyphenylene sulfide (PPS)	26125-40-6	38.0	46.8	-	80.3	-	-	-	19.8	18.7	5.3	3.7	6.7
Polyphenylene sulfide (PPS)		-(1)	3.29(3)		1.53(3)					-(1)	-(1)	-(1)	-(1)
Polyethersulfone (PES)	25154-01-2	-	47.0	-	68.5	-	-	-	21.0	18.3	8.2	6.4	6.3
Polyethersulfone (PES)			-(1)		0.71(2)					0.91(6)	3.10(6)	2.33(6)	2.61(6)
Polybutylene isophthalate	-	-	47.8	-0.080^(c)	-	-	-	-	-	-	-	-	-
Polybutylene isophthalate			-(1)
Nylon 4	24938-56-5	-	48.5	-	-	-	-	-	-	-	-	-	-
Nylon 4			-(1)
Polypropylene isophthalate	-	-	49.3	-0.083^(c)	-	-	-	-	-	-	-	-	-
Polypropylene isophthalate			-(1)
Nylon 2 (polyglycine)	25718-94-9	-	50.1	-	-	-	-	-	-	-	-	-	-
Nylon 2 (polyglycine)			-(1)
Polyacetylene (polyethyne)	-	-	51.5	-	72.0	-	-	-	-	-	-	-	-
Polyacetylene (polyethyne)			0.71(2)		-(1)
Polyacrylamide	9003-05-8	34.3	52.3	-	-	-	-	-	-	-	-	-	-
Polyacrylamide		4.60(2)	-(1)
2-Hydroxyethyl methacrylate (HEMA, ethylene glycol monoacrylate)	867-77-9	-	56.8	-	-	59.0	-	-	-	-	-	-	-
		1.20(2)			-(1)
Nylon 6,12	24936-74-1	-	67.0	-	-	-	-	-	-	-	-	-	-
Nylon 6,12			-(1)

(a) Atactic PP CAS #9003-08-0; isotactic PP CAS #25085-53-4.

(b) S. Wu, J. Macromol. Sci., C10, 1 (1974).

(c) S. Wu, in Polymer Handbook, 3rd Ed., J. Brandrup and E.H. Immergut, eds., Wiley-Interscience, New York, NY, 1989, p. VI: 414-426.

(d) Polybutadiene data for carboxyl end group; S. Wu, in Polymer Handbook, 3rd Ed., J. Brandrup and E.H. Immergut, eds., Wiley-Interscience, New York, NY, 1989, p. VI: 414-426.

(e) Polybutadiene data for methyl ester end group; S. Wu, in Polymer Handbook, 3rd Ed., J. Brandrup and E.H. Immergut, eds., Wiley-Interscience, New York, NY, 1989, p. VI: 414-426.

(f) Aluminum foil, while obviously not a polymer, is included due to its widespread use in package converting and other industries.

⁽¹⁾ Names which are most widely used to describe the material or family of materials (e.g., polyurethanes and epoxies) at hand are preferred here. Commonly used acronyms and synonyms are also shown.

⁽²⁾ CAS (Chemical Abstract Series) numbers are shown where available. In a number of instances, more than one CAS number is assigned to a given polymer — in some cases the details and nuances of these divergences are not at all clear. We have tried to reference the CAS number which appears to have the widest use with reference to the solid state properties of the given polymer.

⁽³⁾ γ_c: Critical surface tension in mJ/m² (equivalent to dynes/cm), generally determined by the Zisman method (regression of the cosine of the contact angle), or by the wetting tension method (using solutions of 2-ethoxyethanol and formamide, per ASTM Std. D-2578).

⁽⁴⁾ γ_s: Surface free energy in mJ/m² (equivalent to dynes/cm), as measured, estimated, and calculated by a wide variety of methods and theories.

⁽⁵⁾ dγ/dt: Change in surface energy in mJ/m² (equivalent to dynes/cm) per degree Kelvin (or Celsius).

⁽⁶⁾ θ_W^Y: Equilibrium (or Young's) contact angle with water, in degrees.

⁽⁷⁾ θ_W^A: Advancing contact angle with water, in degrees.

⁽⁸⁾ θ_W^R: Retreating contact angle with water, in degrees.

⁽⁹⁾ dθ_W: Contact angle hysteresis (difference between advancing and retreating) with water, in degrees.

⁽¹⁰⁾ δ: Total Hansen solubility parameter (square root of the sum of squares of the average values for dispersion, polar, and hydrogen bonding components), in MPa^1/2 (equivalent to joules/cubic centimeter; 2.0455 x (cal/cc)^1/2) @ 20-25^oC (293.15-298.15 K). All data from Hansen Solubility Parameters: A User's Handbook, 2nd Ed., C.M. Hansen, CRC Press, Boca Raton, FL, 2007.

⁽¹¹⁾ δ_D: Hansen dispersion solubility parameter, in MPa^1/2 (equivalent to joules/cubic centimeter; 2.0455 x (cal/cc)^1/2) @ 20-25^oC (293.15-298.15 K). All data from Hansen Solubility Parameters: A User's Handbook, 2nd Ed., C.M. Hansen, CRC Press, Boca Raton, FL, 2007.

⁽¹²⁾ δ_P: Hansen polar solubility parameter, in MPa^1/2 (equivalent to joules/cubic centimeter; 2.0455 x (cal/cc)^1/2) @ 20-25^oC (293.15-298.15 K). All data from Hansen Solubility Parameters: A User's Handbook, 2nd Ed., C.M. Hansen, CRC Press, Boca Raton, FL, 2007.

⁽¹³⁾ δ_H: Hansen hydrogen bonding solubility parameter, in MPa^1/2 (equivalent to joules/cubic centimeter; 2.0455 x (cal/cc)^1/2) @ 20-25^oC (293.15-298.15 K). All data from Hansen Solubility Parameters: A User's Handbook, 2nd Ed., C.M. Hansen, CRC Press, Boca Raton, FL, 2007.

⁽¹⁴⁾ R_o: Interaction radius. All data from Hansen Solubility Parameters: A User's Handbook, 2nd Ed., C.M. Hansen, CRC Press, Boca Raton, FL, 2007.